RED LINE EMITTING COMPLEX FLUORIDE PHOSPHORS ACTIVATED WITH Mn4+

ABSTRACT

New phosphor materials including a complex fluoride phosphor activated with Mn 4+  which may include at least one of (A) A 2 [MF 7 ]:Mn 4+ , wherein A=Li, Na, K, Rb, Cs, NH 4 , or a combination thereof, and M=Nb, Ta or a combination thereof; and (B) A 3 [XF 6 ]:Mn 4+ , wherein A=Li, Na, K, Rb, Cs, NH 4 , or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof.

BACKGROUND OF THE INVENTION

The present exemplary embodiments relate to phosphor compositions, particularly phosphors for use in lighting applications. More particularly, the present embodiments relate to red emitting phosphors and a lighting apparatus employing these phosphors.

Light emitting diodes (LEDs) are semiconductor light emitters often used as a replacement for other light sources, such as incandescent lamps. They are particularly useful as display lights, warning lights and indicator lights or in other applications where colored light is desired. The color of light produced by an LED is dependent on the type of semiconductor material used in its manufacture.

Colored semiconductor light emitting devices, including light emitting diodes and lasers (both are generally referred to herein as LEDs), have been produced from Group III-V alloys such as gallium nitride (GaN). With reference to the GaN-based LEDs, light is generally emitted in the UV to green range of the electromagnetic spectrum. Until recently, LEDs have not been suitable for lighting uses where a bright white light is needed, due to the inherent color of the light produced by the LED.

Recently, techniques have been developed for converting the light emitted from LEDs to useful light for illumination purposes. In one technique, the LED is coated or covered with a phosphor layer. A phosphor is a luminescent material that absorbs radiation energy in a portion of the electromagnetic spectrum and emits energy in another portion of the electromagnetic spectrum. Phosphors of one important class are crystalline inorganic compounds of very high chemical purity and of controlled composition to which small quantities of other elements (called “activators”) have been added to convert them into efficient fluorescent materials. With the right combination of activators and inorganic compounds, the color of the emission can be controlled. Most useful and well-known phosphors emit radiation in the visible portion of the electromagnetic spectrum in response to excitation by electromagnetic radiation outside the visible range.

By interposing a phosphor excited by the radiation generated by the LED, light of a different wavelength, e.g., in the visible range of the spectrum, may be generated. Colored LEDs are often used in toys, indicator lights and other devices. Continuous performance improvements have enabled new applications for LEDs of saturated colors in traffic lights, exit signs, store signs, and the like.

In addition to colored LEDs, a combination of LED generated light and phosphor generated light may be used to produce white light. The most popular white LEDs consist of blue emitting GaInN chips. The blue emitting chips are coated with a phosphor that converts some of the blue radiation to a complementary color, e.g. a yellowish emission. Together, the blue and yellowish radiation produces a white light. There are also white LEDs that utilize a near UV emitting chip and a phosphor blend including red, green and blue emitting phosphors designed to convert the UV radiation to visible light.

Known light emitting devices comprise a blue light-emitting LED having a peak emission wavelength in the near blue range (from about 440 nm to about 480 nm) combined with a yellow light-emitting phosphor, such as cerium(III) doped yttrium aluminum garnet (“YAG:Ce”), a cerium(III) doped terbium aluminum garnet (“TAG:Ce”), or a europium(II) doped barium orthosilicate (“BOS:Eu”). The phosphor absorbs a portion of the radiation emitted from the LED and converts the absorbed radiation to a yellow light. The remainder of the blue light emitted by the LED is transmitted through the phosphor and is mixed with the yellow light emitted by the phosphor. A viewer perceives the mixture of blue and yellow light as a white light. The total of the light from the phosphor material and the LED chip provides a color point with corresponding color coordinates (x and y) and correlated color temperature (CCT), and its spectral distribution provides a color rendering capability, measured by the color rendering index (CRI).

Such systems can be used to make light sources having CCTs of >4500 K and CRIs ranging from about 70-82, with luminous efficacy of radiation (“LER”, also referred to as luminosity) of about 330 lm/W_(opt). While this range is suitable for many applications, general illumination sources usually require lower CCTs and higher CRIs, preferably with similar or better LER.

One particularly preferred application of LED devices made from blue emitting chips and yellow emitting phosphors is for backlights, e.g. in cellular phones, personal digital assistants, and the like. These applications require high CCT values (greater than 5000K), which are readily provided by the aforementioned LEDs, with LER values of 280 lm/W_(opt) or greater. However, due to the use of yellow phosphors (e.g. having a peak emission between 550 nm and 610 nm), the spectra of these LEDs contain excessive emission in the yellow region of the spectrum, which strongly reduces the color gamut of the backlight.

The color gamut is the area spanned between the color points of the red, green and blue pixels of the display in a chromaticity diagram, e.g. the CIE 1931 x, y diagram. The historical “golden standard” for displays is the NTSC gamut, defined by 3 sets of color point coordinates (x=0.674 and y=0.326 for red, x=0.218 and y=0.712 for green, and x=0.140 and y=0.080 for blue in the CIE 1931 x,y chromaticity diagram). Generally, a gamut greater than 70% of NTSC is considered acceptable for many backlighting applications, and a gamut greater than 90% of NTSC is considered acceptable for most any such application.

In order to improve the gamut of LED backlights using yellow phosphors, the yellow light is filtered out, thereby reducing the effective LER of the LED backlight. It would be therefore beneficial to develop LED backlights that can provide LER of 280 lm/W_(opt) or greater at CCT>5000K without having yellow phosphors in the package. Red line-emitting phosphors would be particularly suitable for obtaining simultaneously such values for LER and CCT when used with blue or near-UV LED chips, in conjunction with at least a green-emitting and a blue-emitting phosphor, as needed.

Other white light LED lighting systems use a UV or visible light LED chip along with a blend of red, green, and/or blue phosphors that can be efficiently excited by near-UV radiation to make white light.

The CRI is commonly defined as a mean value for 8 standard color samples (R₁₋₈), usually referred to as the General Color Rendering Index and abbreviated as R_(a), although 14 standard color samples are specified internationally and one can calculate a broader CRI (R₁₋₁₄) as their mean value. In particular, the R₉ value, measuring the color rendering for the strong red, is very important for a range of applications, especially of a medical nature.

As the CCT is lowered and/or the CRI is increased, the LER value for phosphor downconverted LEDs generally decreases, leading to values for “warm white” LEDs (of CCT<4500K) significantly lower than those for “cool white” LEDs (of CCT>4500K). The LER values can be improved by using red phosphors having a line emission spectrum, as opposed to red phosphors with a broadband emission. A significant portion of the emitted energy of the latter phosphors tends to fall into the deep red part of the spectrum where the sensitivity of the human eye is very low, thereby decreasing the LER value.

In many light applications, phosphors with line emission spectra (e.g. Y₂O₃: Eu³⁺) are thus preferred as the red component because it maximizes LER at acceptable CRI values (e.g. 80-86), over the CCT range of interest (e.g. 2700-6500K). Current red fluorescent lamp phosphors doped with Eu³⁺ such as Y₂O₃: Eu³⁺ has little absorption of near-UV (370-420 nm) light, leading to larger light losses due to scattering by phosphor powders. A deep red line emitting oxyfluoride phosphor, e.g. 3.5MgO*0.5MgF₂*GeO₂: Mn⁴⁺ (MFG) can be used in LED lamps, but with considerable impact to LER, due to much of its emission occurring too far in the deeper red region of the spectrum (beyond 650 nm). Other similar phosphors based on oxide and oxyhalide host lattices doped with Mn⁴⁺ also have a main emission peak at a wavelength greater than 650 nm. It would be preferable to use red phosphors with line emission maxima at lower wavelengths, e.g. in the 610 to 650 nm range, having good absorbance for the LED chip emitting in the UV to blue range. This improves the LER while maintaining the general CRI at 80 or above, as well as minimizes scattering losses within the LED package.

Thus, a continuing need exists for new red line-emitting phosphors and their blends for use in conjunction with UV and visible LED chips displaying high quantum efficiency to produce white-light LEDs having both a high CRI and an improved LER at any given CCT, as well as backlight LEDs with minimal yellow emission and high LER.

BRIEF SUMMARY

In a first aspect, there is provided a backlight emitting device including a semiconductor light source; wherein the backlight comprises a red line-emitting phosphor selected from (a) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; or (b) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof; a green emitting phosphor having a peak emission wavelength between 510 and 550 nm; and either a) a blue LED chip having a peak emission wavelength between 440 and 480 nm, or b) a blue emitting phosphor having a peak emission wavelength between 440 and 480 nm and a violet to near-UV emitting LED chip having a peak emission wavelength from about 370 nm to about 440 nm.

In a second aspect, there is provided a light emitting device including a semiconductor light source and a complex fluoride phosphor material activated with Mn⁴⁺. In one embodiment, the complex fluoride phosphor material comprises at least one of: (a) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; or (b) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof.

In a third aspect, there is provided a phosphor blend including at least one of the above complex fluoride phosphors activated with Mn⁴⁺ and at least one additional phosphor.

In a fourth aspect, there is provided a phosphor material including at least one of: (a) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; or (b) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic cross-sectional view of an illumination system.

FIG. 2 is a schematic cross-sectional view of an illumination system.

FIG. 3 is a schematic cross-sectional view of an illumination system

FIG. 4 is a cutaway side perspective view of an illumination system.

FIG. 5 is a graph of the excitation spectrum of a K₂[NbF₇]:Mn⁴⁺ phosphor.

FIG. 6 is a graph of the emission spectrum of a K₂[NbF₇]:Mn⁴⁺ phosphor.

FIG. 7 is a graph of the excitation spectrum of a K₂[TaF₇]:Mn⁴⁺ phosphor.

FIG. 8 is a graph of the emission spectrum of a K₂[TaF₇]:Mn⁴⁺ phosphor.

FIG. 9 is a graph of the excitation spectrum of a K₃[BiF₆]:Mn⁴⁺ phosphor.

FIG. 10 is a graph of the emission spectrum of a K₃[BiF₆]:Mn⁴⁺ phosphor.

FIG. 11 is a graph of the excitation spectrum of a K₃[YF₆]:Mn⁴⁺ phosphor.

FIG. 12 is a graph of the emission spectrum of a K₃[YF₆]:Mn⁴⁺ phosphor.

FIG. 13 is a graph of the excitation spectrum of a K₃[LaF₆]:Mn⁴⁺ phosphor.

FIG. 14 is a graph of the emission spectrum of a K₃[LaF₆]:Mn⁴⁺ phosphor.

FIG. 15 is a graph of the excitation spectrum of a K₃[GdF₆]:Mn⁴⁺ phosphor

FIG. 16 is a graph of the emission spectrum of a K₃[GdF₆]:Mn⁴⁺ phosphor.

FIG. 17 is a graph of the power distribution spectrum of a particularly preferred embodiment.

FIG. 18 is a schematic perspective view of a surface mounted device (SMD) backlight LED.

DETAILED DESCRIPTION OF THE EXEMPLARY EMBODIMENTS

Phosphors convert radiation (energy) to visible light. Different combinations of phosphors provide different colored light emissions. Novel phosphor compositions and blends are presented herein as well as their use in LED and other light sources.

The color of the generated visible light is dependent on the particular components of the phosphor material. The phosphor material may include only a single phosphor composition or two or more phosphors of basic color, for example a particular mix with one or more of a yellow and red phosphor to emit a desired color (tint) of light. As used herein, the terms “phosphor” and “phosphor material” may be used to denote both a single phosphor composition as well as a blend of two or more phosphor compositions.

It was determined that an LED lamp that produces a white light would be useful to impart desirable qualities to LEDs as light sources. Therefore, in one embodiment, a luminescent material phosphor conversion material blend (phosphor blend) coated LED chip is disclosed for providing white light. The phosphor blends presented in this embodiment enable white light with an optimal combination of CRI and LER at any CCT of interest, when excited by radiation from about 250 to 550 nm as emitted by a near UV to green LED.

With reference to FIG. 1, an exemplary LED based light emitting assembly or lamp 10 is shown in accordance with one preferred structure of the present invention. The light emitting assembly 10 comprises a semiconductor UV or visible radiation source, such as a light emitting diode (LED) chip 12 and leads 14 electrically attached to the LED chip. The leads 14 may comprise thin wires supported by a thicker lead frame(s) 16 or the leads may comprise self supported electrodes and the lead frame may be omitted. The leads 14 provide current to the LED chip 12 and thus cause the LED chip 12 to emit radiation.

The lamp may include any semiconductor visible or UV light source that is capable of producing white light when its emitted radiation is directed onto the phosphor. The preferred peak emission of the LED chip in the present invention will depend on the identity of the phosphors in the disclosed embodiments and may range from, e.g., 250-550 nm. In one preferred embodiment, however, the emission of the LED will be in the near UV to blue-green region and have a peak wavelength in the range from about 370 to about 500 nm.

In one embodiment, the chip is a blue LED with a peak emission wavelength between 440 and 480 nm. In a second embodiment, the LED is a violet to near-UV emitting LED chip having a peak emission wavelength from about 370 nm to about 440 nm.

Typically then, the semiconductor light source comprises an LED doped with various impurities. Thus, the LED may comprise a semiconductor diode based on any suitable III-V, II-VI or IV-IV semiconductor layers and having a peak emission wavelength of about 250 to 550 nm.

Preferably, the LED may contain at least one semiconductor layer comprising GaN, ZnO or SiC. For example, the LED may comprise a nitride compound semiconductor represented by the formula In_(i)Ga_(j)Al_(k)N (where 0≦i; 0≦j; 0≦k and i+j+k=1) having a peak emission wavelength greater than about 250 nm and less than about 550 nm. Such LED semiconductors are known in the art. The radiation source is described herein as an LED for convenience. However, as used herein, the term is meant to encompass all semiconductor radiation sources including, e.g., semiconductor laser diodes.

Although the general discussion of the exemplary structures of the invention discussed herein are directed toward inorganic LED based light sources, it should be understood that the LED chip may be replaced by an organic light emissive structure or other radiation source unless otherwise noted and that any reference to LED chip or semiconductor is merely representative of any appropriate radiation source.

The LED chip 12 may be encapsulated within a shell 18, which encloses the LED chip and an encapsulant material 20. The shell 18 may be, for example, glass or plastic. Preferably, the LED 12 is substantially centered in the encapsulant 20. The encapsulant 20 is preferably an epoxy, plastic, low temperature glass, polymer, thermoplastic, thermoset material, resin or other type of LED encapsulating material as is known in the art. Optionally, the encapsulant 20 is a spin-on glass or some other material having a high index of refraction. In one embodiment, the encapsulant material 20 is a polymer material, such as epoxy, silicone, or silicone epoxy, although other organic or inorganic encapsulants may be used. Both the shell 18 and the encapsulant 20 are preferably transparent or substantially optically transmissive with respect to the wavelength of light produced by the LED chip 12 and a phosphor material 22 (described below). In an alternate embodiment, the lamp 10 may only comprise an encapsulant material without an outer shell 18. The LED chip 12 may be supported, for example, by the lead frame 16, by the self supporting electrodes, the bottom of the shell 18, or by a pedestal (not shown) mounted to the shell or to the lead frame.

The structure of the illumination system includes a phosphor material 22 radiationally coupled to the LED chip 12. Radiationally coupled means that the elements are associated with each other so that at least part of the radiation emitted from one is transmitted to the other.

This phosphor material 22 is deposited on the LED 12 by any appropriate method. For example, a suspension of the phosphor(s) can be formed, and applied as a phosphor layer to the LED surface. In one such method, a silicone, epoxy or other matrix material is used (either directly or diluted with an organic solvent, e.g. acetone, MIBK or butyl acetate) to create a slurry in which the phosphor particles are randomly suspended and placed around the LED. This method is merely exemplary of possible positions of the phosphor material 22 and LED 12. Thus, the phosphor material 22 may be coated over or directly on the light emitting surface of the LED chip 12 by coating and drying or curing the phosphor suspension over the LED chip 12. Both the shell 18 and the encapsulant 20 should be transparent to allow light 24 to be transmitted through those elements. Although not intended to be limiting, the median particle size of the phosphor material as measured using light scattering methods or via microscope (electron or optical) measurements may be from about 1 to about 20 microns.

FIG. 2 illustrates a second preferred structure of the system according to the preferred aspect of the present invention. Corresponding numbers from FIGS. 1-4 (e.g. 12 in FIG. 1 and 112 in FIG. 2) relate to corresponding structures in each of the figures unless otherwise stated. The structure of the embodiment of FIG. 2 is similar to that of FIG. 1, except that the phosphor material 122 is interspersed within the encapsulant material 120, instead of being formed directly on the LED chip 112. The phosphor material (in the form of a powder) may be interspersed within a single region of the encapsulant material 120 or, more preferably, throughout the entire volume of the encapsulant material. Radiation 126 emitted by the LED chip 112 mixes with the light emitted by the phosphor material 122, and the mixed light appears as white light 124. If the phosphor is to be interspersed within the encapsulant material 120, then a phosphor powder may be added to a polymer precursor, loaded around the LED chip 112, and then the polymer precursor may be cured to solidify the polymer material. Other known phosphor interspersion methods may also be used, such as transfer molding.

FIG. 3 illustrates a third preferred structure of the system according to the preferred aspects of the present invention. The structure of the embodiment shown in FIG. 3 is similar to that of FIG. 1, except that the phosphor material 222 is coated onto a surface of the shell 218, instead of being formed over the LED chip 212. The phosphor material is preferably coated on the inside surface of the shell 218, although the phosphor may be coated on the outside surface of the shell, if desired. The phosphor material 222 may be coated on the entire surface of the shell or only a top portion of the surface of the shell. The radiation 226 emitted by the LED chip 212 mixes with the light emitted by the phosphor material 222, and the mixed light appears as white light 224. Of course, the structures of FIGS. 1-3 may be combined and the phosphor may be located in any two or all three locations or in any other suitable location, such as separately from the shell or integrated into the LED.

In any of the above structures, the lamp 10 may also include a plurality of scattering particles (not shown), which are embedded in the encapsulant material. The scattering particles may comprise, for example, Al₂O₃ particles (such as alumina powder) or TiO₂ particles. The scattering particles effectively scatter the coherent light emitted from the LED chip, preferably with a negligible amount of absorption.

As shown in a fourth preferred structure in FIG. 4, the LED chip 412 may be mounted in a reflective cup 430. The cup 430 may be made from or coated with a reflective material, such as alumina, titania, or other dielectric powder known in the art. A preferred reflective material is Al₂O₃. The remainder of the structure of the embodiment of FIG. 4 is the same as that of any of the previous Figures, and includes two leads 416, a conducting wire 432 electrically connecting the LED chip 412 with the second lead, and an encapsulant material 420.

Another preferred structure (particularly for backlight applications) is a surface mounted device (“SMD”) type light emitting diode 550, e.g. as shown in FIG. 18. This SMD is of a “side-emitting type” and has a light emitting window 552 on a protruding portion of a light guiding member 554. The SMD type light emitting diodes 550 can be made by disposing LEDs that have been formed beforehand by flow soldering or the like on a glass epoxy substrate, whereon an electrically conductive pattern has been formed and covering said LED with the window 552. There are also “top-emitting” SMD packages known in the art that are also suitable for use in the present embodiments, e.g. those produced by Nichia Corporation. An SMD package may comprise an LED chip as defined above, and a phosphor material as discussed below that is excited by the light emitted from the LED chip.

In one embodiment, there is provided a novel phosphor material, which may be used in the phosphor composition in the above described devices. The phosphor material is a complex fluoride phosphor activated with Mn⁴⁺ and may comprise one or more of (a) A₂[MF₇]: Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; or (b) A₃[XF₆]: Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, lanthanide, Bi, or a combination thereof.

By “complex fluoride phosphor”, it is meant that the phosphor is a coordination compound, containing at least one coordination center (e.g. Nb or Ta in the first phosphor above), surrounded by fluoride ions acting as ligands, and charge-compensated by counter ions (e.g. A in the examples above) as necessary. Complex fluorides are occasionally written down as a combination of simple, binary fluorides (e.g. 3KF*LaF₃ instead of K₃[LaF₆]), but such a representation does not indicate the coordination number (in this example, 6) for the ligands around the coordination center. The square brackets (occasionally omitted for simplicity) indicate that the complex ion they encompass is a new chemical species, different from the simple fluoride ion. The activator ion (Mn⁴⁺) also acts as a coordination center, substituting part of the centers of the host lattice, e.g. La³⁺. The host lattice (including the counter ions) can further modify the excitation and emission properties of the activator ion.

When used with an LED chip emitting at from 250 to 550 nm, and one or more additional phosphors (such as blue and green emitting phosphors), the use of the above phosphor material allows for a white LED. The additional phosphors that can be used with the above described phosphors are described in more detail below.

Non-limiting exemplary Mn⁴⁺ activated compositions of this embodiment include: K₂[NbF₇]: Mn⁴⁺, K₂[TaF₇]: Mn⁴⁺, K₃[BiF₆]: Mn⁴⁺, K₃[YF₆]: Mn⁴⁺, K₃[LaF₆]: Mn⁴⁺, and K₃[GdF₆]: Mn⁴⁺. FIGS. 5-16 show the excitation and emission spectra of these phosphors. The emission spectra are measured under 365 nm excitation.

The above described complex fluoride phosphor compositions activated with Mn⁴⁺ can be prepared by using appropriate raw materials in a ratio sufficient to ensure the desired incorporation level of the activator ion (e.g. between 0.1 and 30 mol. % of the total M content, more preferably between 2 and 15 mol %).

The novel complex fluoride phosphors disclosed herein are prepared by activation of the corresponding host lattice with Mn⁴⁺, typically by co-precipitation at 100° C. by evaporating a common solution in aqueous HF (e.g. 40-50% HF by weight), or at room temperature by soaking the host lattice material with a solution of K₂[MnF₆] in aqueous HF, followed by evaporation to dryness. The requisite host lattices may be commercially obtained, e.g. as in the case of K₂[MF₇] where M=Nb or Ta, or synthesized from the corresponding simple fluorides (e.g. XF₃ where X==Sc, Y, La, lanthanide, Bi, or a combination thereof) and KF by heating (e.g. at 600° C. for 4 hrs). Adventitious amounts of oxygen ions or water may also enter the host lattices and become part of them but are typically not written into the general formulas, for the sake of simplicity. Any such amounts are implicitly incorporated herein. The crude phosphor may be then milled (preferably dry-milled) to a desired particle size, washed with an organic solvent (e.g. ethanol or acetone) to remove any remaining amounts of HF and dried on the air prior to use in LEDs.

In addition, it is possible that a variety of other starting materials may be used to produce the inventive complex fluoride phosphors via co-crystallization from aqueous solution of HF and/or other fluorides (e.g. prepared in-situ or ex-situ from oxides, hydroxides, alkoxides, carbonates and binary fluorides or hydrogen fluorides of the metal constituents), and permanganates or manganates with a stoichiometric amount of H₂O₂ or other peroxide to provide the Mn activator in the proper oxidation state (+4). The examples of complex fluoride phosphors doped with Mn⁴⁺ shown herein are not meant to be limiting. Other constituent ions may be used to build the complex fluoride host lattice (as the coordination center or the counter ion), provided they do not introduce electronic or vibrational transitions deleterious to the phosphor excitation and/or emission upon activation with Mn⁴⁺.

EXAMPLES Preparation of A₃[ScF₆]:Mn⁴⁺ Phosphors where A=Na, K, Rb, Cs

A stoichiometric amount of Sc₂O₃ needed for 10 g of dry sample was introduced in a 25 ml 70% HF-acid and the suspension was heated to the boiling point for one hour. The stoichiometric amount of the corresponding alkali metal carbonate was added gradually to the suspension. The suspension was evaporated to dryness in a water bath and ground in a mortar. The dry residue was put into a platinum test tube, which was placed in a larger quartz tube furnace. The temperature of the furnace was increased to 300° C. and the sample was heated at this temperature for ½ hour under Ar. For the K, Rb and Cs complexes, the temperature was then increased further to 600° C. in Ar-atmosphere and held for 3 hours, after which the furnace cooled to room temperature. The obtained products were ground in a mortar.

Two phosphor samples for each alkali metal complex were prepared with 4 mol % and 8 mol % Mn⁴⁺. The appropriate amount of activator complex K₂MnF₆ and the matrix for a 10 g sample (see Table 1) was mixed with 2 ml 40% HF-acid and was stirred at regular intervals for 3 hours. After that, the samples were evaporated to dryness in a water bath.

TABLE 1 Amounts of raw materials for 10 g sample of A₃[ScF₆]:Mn⁴⁺. Sample Precursors [g] Sc complex [g] K₂MnF₆ [g] HF [ml] Na₃ScF₆ 3.0255 6.9755 — — 25  Sc₂O₃ Na₂CO₃ (70%) 0.96 Na₃ScF₆•0.04 — — 9.5677 0.4323 2 K₂MnF₆ Na₃ScF₆ (40%) 0.92 Na₃ScF₆•0.08 — — 9.1384 0.8616 2 K₂MnF₆ Na₃ScF₆ (40%) K₃ScF₆ 2.4962 7.5049 — — 25  Sc₂O₃ K₂CO₃ (70%) 0.96 K₃ScF₆•0.04 — — 9.6407 0.3593 2 K₂MnF₆ K₃ScF₆ (40%) 0.92 K₃ScF₆•0.08 — — 9.2782 0.7218 2 K₂MnF₆ K₃ScF₆ (40%) Rb₃ScF₆ 1.5276 7.6753 — — 25 Sc₂O₃ Rb₂CO₃ (70%) 0.96 Rb₃ScF₆•0.04 — — 9.7518 0.2419 2 K₂MnF₆ Rb₃ScF₆ (40%) 0.92 Rb₃ScF₆•0.08 — — 9.5081 0.4919 2 K₂MnF₆ Rb₃ScF₆ (40%) Cs₃ScF₆ 1.2365 8.7639 — — 25  Sc₂O₃ Cs₂CO₃ (70%) 0.96 Cs₃ScF₆•0.04 — — 9.8187 0.3710 2 K₂MnF₆ Cs₃ScF₆ (40%) 0.92 Cs₃ScF₆•0.08 — — 9.6290 0.3710 2 K₂MnF₆ Cs₃ScF₆ (40%) Preparation of A₃[YF₆]:Mn⁴⁺ Phosphors where A=Na, K.

The precursors were alkali carbonates (Aldrich and Fluka p.a.) and yttrium carbonate, prepared by an ion-exchange interaction between NH₄HCO₃ and Y(NO₃)₃ and analyzed by the loss on ignition (LOI) method.

The calculated amounts of Y₂(CO₃)₃ and A₂CO₃ (A=Na, K) for 10 g of dry sample were dissolved in 40 ml 40% HF-acid and evaporated to dryness on a water bath. The dry residue was fired in a tube furnace, as described in the preceding example. The obtained products were ground in a mortar.

NaYF₄ was also prepared by mixing 1 M solution of Y(NO₃)₃, 40% HF-acid and water solution of Na₂CO₃ in stoichiometric amounts. The mixed solution was heated and stirred over 4 hours. After decantation, the sediment was washed with distilled water and vacuum filtered over a Buchner funnel. This procedure was repeated 3 times. The precipitate was then dried in an oven at 100° C.

TABLE 2 Amounts of raw materials for 10 g samples of A₃[YF₆]:Mn⁴⁺. Precursors A3YF6 Y2(CO3)3, [g] V40% AYF4 Activat. 1M Y(NO3)3, A2CO3 HF AY2F6 [g] Sample [,ml] [g] [ml] [g] K2MnF6 NaYF4 Y(NO3)3 Na2CO3 40 — — 3.6781 11.6955 0.96 — — 2 9.4800 0.5192 NaYF4•0.04 K2MnF6 0.92 — — 2 8.9733 1.0258 NaYF4•0.08 K2MnF6 K3YF6 Y2(CO3)3 K2CO3K 40 — — 5.5874 6.4742 0.96 — — 2 9.6883 0.3117 K3YF6•0.04 K2MnF6 0.92 — — 2 9.3708 0.6292 K3YF6•0.08 K2MnF6

The calculated amount of activator complex K₂MnF₆ and the matrix for 10 g of dry sample (see Table 2) was mixed with 2 ml 40% HF acid and was stirred periodically during 3 hours. Finally the samples were dried as in the previous example.

Preparation of A₃[BiF₆]:Mn⁴⁺ Phosphors (where A=Li, Na, K, Rb, Cs, NH₄).

The precursor, BiF₃, was obtained from Bi(NO₃)₃.5H₂O and 40% aqueous HF. 10 g Bi(NO₃)₃.5H₂O were dissolved in 100 ml 40% HF acid and heated on a water bath for 1 hour. The precipitate was washed 3 times with 100 ml of alcohol through decantation, vacuum filtered over a Buchner funnel, then dried in an oven at 100° C.

Stoichiometric amounts of BiF₃ and A₂CO₃ (A=Li, Na, K, Rb, Cs) calculated for 10 g of dry sample (see Table 3) were added to 25 ml of 40% HF-acid and evaporated to dryness. The samples were fired in two steps in a tube furnace under Ar. The first step was a 1 hour firing at 400° C. with a second step for 2 hrs, at 550° C. for the Li complex, 600° C. for the Na complex, 700° C. for the K complex, 750° C. for the Rb complex, and 600° C. for the Cs complex. The obtained products were ground in a mortar.

A sample of the ammonium complex was prepared from a stoichiometric mixture of BiF₃ and (NH₄)₂CO₃ in 25 ml 40% HF-acid (see Table 3), evaporated to dryness in an oil bath at 130° C.

TABLE 3 Amounts of raw materials for 10 g samples of A₃[BiF₆]:Mn⁴⁺. Bi - K₂MnF₆ 40% Formula Precursors, g complex [g] [g] HF [ml] Li₃BiF₆ 7.7365 BiF₃ 3.2239 — — 25 Li₂CO₃ 0.96 Li₃BiF₆ — — 9.7092 0.2908 2 0.04 K₂MnF₆ Li₃BiF₆ 0.92 Li₃BiF₆ — — 9.4117 0.5883 2 0.08 K₂MnF₆ Li₃BiF₆ Na₃BiF₆ 6.7862 BiF₃ 4.0564 — — 25 Na₂CO₃ 0.96 Na₃BiF₆ — — 9.7445 0.2555 2 0.04 K₂MnF₆ Na₃BiF₆ 0.92 Na₃BiF₆•0.08 — — 9.4728 0.5272 2 K₂MnF₆ Na₃BiF₆ K₃BiF₆ 6.0413 BiF₃ 4.7089 — — 25 K₂CO₃ 0.98 K₃BiF₆•0.02 — — 9.8867 0.1133 2 K₂MnF₆ K₃BiF₆ 0.96 K₃BiF₆•0.04 — — 9.7715 0.2285 2 K₂MnF₆ K₃BiF₆ 0.92 K₃BiF₆•0.08 — — 9.5346 0.4654 2 K₂MnF₆ K₃BiF₆ K_(0.3)Bi_(0.7)F_(2.4) 9.1441 1.0182 — — 25 BiF₃ K₂CO₃ 0.96 K_(0.3)Bi_(0.7)F_(2.4)•0.04 — — 9.5186 0.4814 2 K₂MnF₆ K_(0.3)Bi_(0.7)F_(2.4) 0.92 K_(0.3)Bi_(0.7)F_(2.4)•0.08 — — 9.0454 0.9546 2 K₂MnF₆ K_(0.3)Bi_(0.7)F_(2.4) Rb₃BiF₆ 4.5908 5.9793 — — 25 BiF₃ Rb₂CO₃ 0.96 Rb₃BiF₆•0.04 — — 9.8254 0.1746 2 K₂MnF₆ Rb₃BiF₆ 0.92 Rb₃BiF₆•0.08 — — 9.6424 0.3576 2 K₂MnF₆ Rb₃BiF₆ RbBiF₄ 7.1800 3.1172 — — 25 BiF₃ Rb₂CO₃ 0.96 RbBiF₄•0.04 — — 9.7296 0.2704 2 K₂MnF₆ RbBiF₄ 0.92 RbBiF₄•0.08 — — 9.4517 0.5483 2 K₂MnF₆ RbBiF₄ Cs₃BiF₆ 3.6855 BiF₃ 6.7721 — — 25 Cs₂CO₃ 0.96 Cs₃BiF₆•0.04 — — 9.8593 0.1407 2 K₂MnF₆ Cs₃BiF₆ 0.92 Cs₃BiF₆•0.08 — — 9.6424 0.3576 2 K₂MnF₆ Cs₃BiF₆ (NH₄)₃BiF₆ 7.7997 BiF₃ 4.2265 — — 25 (NH₄)₂CO₃ 0.96 (NH₄)₃BiF₆•0.04 — — 9.7069 0.2931 2 K₂MnF₆ (NH₄)₃BiF₆ 0.92 (NH₄)₃BiF₆•0.08 — — 9.4072 0.5928 2 K₂MnF₆ (NH₄)₃BiF₆ NH₄BiF₄ 8.7778 1.5855 — — 25 BiF₃ (NH₄)₂CO₃ 0.96 NH₄BiF₄•0.04 — — 9.6714 0.3286 2 K₂MnF₆ NH₄BiF₄ 0.92 NH₄BiF₄•0.08 — — 9.3378 0.6622 2 K₂MnF₆ NH₄BiF₄

The calculated amounts (for 10 g of sample) of phosphor matrix and K₂MnF₆ in amount for 4 and 8 mol % activation were well mixed with 2 ml 40% HF-acid to a thick paste. This suspension was evaporated to dryness in a water bath.

Preparation of A₃[GdF₆]:Mn⁴⁺ Phosphors where A=Na, K.

The precursors for A₃[GdF₆] were A₂CO₃ carbonates and Gd₂(CO₃)₃ (precipitated from Gd(NO₃)₃ with NH₄HCO₃, taken in 5% stoichiometric excess, and analyzed by the LOI method).

The calculated amounts of Gd₂(CO₃)₃ and A₂CO₃ needed for 10 g of dry sample were dissolved in 25 ml 40% HF-acid and evaporated to dryness on a water bath (see Table 4).

TABLE 4 Amounts of raw materials for 10 g samples of A₃[GdF₆]:Mn⁴⁺. K2MnF6 40% Sample Precursors [g] Gd - complex [g] [g] HF [ml] NaGdF4 7.2680 4.6732 — — 25 Gd2(CO3)3 Na2CO3 0.96 NaGdF4•0.04 — — 9.6137 0.3863 2 K2MnF6 NaGdF4 0.92 NaGdF4•0.08 — — 9.2262 0.7738 2 K2MnF6 NaGdF4 K3GdF6 6.3640 5.3358 — — 25 Gd2(CO3)3 K2CO3 0.96 K3GdF6•0.04 — — 9.7418 0.2582 2 K2MnF6 K3GdF6 0.92 K3GdF6•0.08 — — 9.4759 0.5241 2 K2MnF6 K3GdF6

The host lattice samples were then fired in 2 steps as in the previous examples of A₃[BiF₆]:Mn⁴⁺ phosphors.

Two kinds of phosphor samples were prepared: with 4 mol % and 8 mol % Mn⁴⁺. The calculated amount of activator complex K₂MnF₆ and the matrix for 10 g sample (see table 4) was mixed with 2 ml 40% HF-acid and stirred periodically during 3 hours. After that, each sample was evaporated to dryness on a water bath.

Preparation of K₂[MF₇]:Mn⁴⁺ Phosphors, where M=Nb or Ta.

Commercial reagents K₂NbF₇ and K₂TaF₇ from Aldrich were used as the starting materials. Each heptafluoride was dissolved in 20 ml of 40% HF-acid with added K₂MnF₆ (at either 4 mol % or 8 mol % level, calculated for 10 g of total dry residue). The solutions were evaporated to dryness in an oil bath at 120° C.

The relative amounts of each phosphor in the phosphor blend material of an inventive device can be described in terms of spectral weight. The spectral weight is the relative amount that each phosphor contributes to the overall emission spectra of the phosphor blend. The spectral weight amounts of all the individual phosphors should add up to 1. A preferred blend comprises a spectral weight of from 0.01 to 0.80 of a phosphor having a peak emission of from about 500 to 610 nm, from 0 to 0.19 of an optional phosphor having a peak emission from about 430 to 500 nm (which would not be needed for excitation with a blue or blue-green LED having a peak emission from about 430 to about 500 nm), and the balance of the blend being one of the above described complex fluoride phosphors, as needed to achieve the targeted CCT value. Any known phosphors suitable for use in near-UV to green LED systems and emitting in the above wavelength ranges may be used. Garnets activated with at least Ce3+ (e.g. YAG:Ce, TAG:Ce and their compositional modifications known in the art) are preferred example phosphors with an emission maximum at about 500 to 610 nm. Other preferred phosphors having a peak emission in the latter range are alkaline earth orthosilicates activated with at least Eu²⁺, e.g. (Ba,Sr,Ca)₂SiO₄: Eu²⁺ (“BOS:Eu”) and its compositional modifications known in the art.

It should be noted that various phosphors are described herein in which different elements enclosed in parentheses and separated by commas, such as in the case of (Ba,Sr,Ca)₂SiO₄: Eu²⁺. As understood by those skilled in the art, this type of notation means that the phosphor can include any or all of those specified elements in the formulation in any ratio. That is, this type of notation for the above phosphor, for example, has the same meaning as (Ba_(a)Sr_(b)Ca_(1-a-b))₂SiO₄: Eu²⁺, where a and b can vary from 0 to 1, including the values of 0 and 1.

One or more of the above inventive red line-emitting phosphors having a peak emission wavelength between 610 and 650 nm may be used to prepare a backlight LED, in conjunction with at least a green emitting phosphor (e.g. with a peak emission wavelength between 510 and 550 nm) and either a blue LED chip or a blue emitting phosphor (e.g. with a peak emission wavelength between 440 and 480 nm) and a violet to near-UV emitting LED chip (e.g. having a peak emission wavelength from about 370 nm to about 440 nm).

A non-limiting example of a suitable green emitting phosphor is an alkaline earth thiogallate, thioaluminate or a solid solution thereof activated with Eu2+, e.g. strontium thiogallate activated with Eu2+ (“STG”) SrGa₂S₄: Eu²⁺, and a non-limiting example of a suitable blue-emitting phosphor is strontium chloroapatite activated with Eu²⁺ (“SECA”) Sr₅(PO₄)₃Cl: Eu²⁺.

Backlights made with complex fluoride phosphor activated with Mn⁴⁺ can have LER equivalent or better than that of typical blue chip/yellow phosphor LEDs. However, unlike the yellow phosphor based LEDs, they will have very little emission in the yellow region of the spectrum which is undesirable for backlighting applications, as explained earlier. Preferably, such backlights will have a gamut greater than 70% that of the NTSC standard, and more preferably greater than 90% that of the NTSC standard in the CIE 1931 x, y diagram.

In addition, other phosphors emitting throughout the visible spectrum region, at wavelengths substantially different from those of the phosphors described in the present invention, may be used in the blend to customize the white color of the resulting light and produce sources with improved light quality. While not intended to be limiting, suitable phosphors for use in the blend with the present phosphors include:

(Ba,Sr,Ca)₅(PO₄)₃(Cl, F, Br, OH):Eu²⁺, Mn²⁺ (Ba,Sr,Ca)BPO₅:Eu²⁺,Mn²⁺

(Sr,Ca)₁₀(PO₄)₆*νB₂O₃: Eu²⁺ (wherein 0<ν≦1)

Sr₂Si₃O₈*2SrCl₂:Eu²⁺ (Ca,Sr,Ba)₃MgSi₂O₈:Eu²⁺,Mn²⁺ BaAl₈O₁₃:Eu²⁺ 2SrO*0.84P₂O₅*0.16B₂O₃: Eu²⁺ (Ba,Sr,Ca)MgAl₁₀O₁₇:Eu²⁺,Mn²⁺ (Ba,Sr,Ca)Al₂O₄:Eu²⁺ (Y,Gd,Lu,Sc,La)BO₃:Ce³⁺,Tb³⁺

(Ba,Sr,Ca)₂Si_(1−ξ)O_(4−2ξ):Eu²⁺ (wherein 0≦ξ≦0.2)

(Ba,Sr,Ca)₂(Mg,Zn)Si₂O₇:Eu²⁺ (Sr,Ca,Ba)(Al,Ga,In)₂S₄:Eu²⁺

(Y,Gd,Tb,La,Sm,Pr,Lu)₃(Sc,Al,Ga)_(5−α)O_(12−3/2α):Ce³⁺ (wherein 0≦α≦0.5) (Lu,Sc,Y,Tb)_(2−u−v)Ce_(v)Ca_(1+u)Li_(w)Mg_(2−w)P_(w)(Si,Ge)_(3−w)O_(12−u/2) where −0.5≦u≦1; 0≦v≦0.1; and 0≦w≦0.2

(Ca,Ba,Sr)Si₂O₂N₂:Eu²⁺,Ce³⁺ (Ca,Sr)₈(Mg,Zn)(SiO₄)₄Cl₂:Eu²⁺,Mn²⁺

Na₂Gd₂B₂O₇:Ce³⁺,Tb³⁺ (Sr,Ca,Ba,Mg,Zn)₂P₂O₇:Eu²⁺,Mn²⁺

(Gd,Y,Lu,La)₂O₃:Eu³⁺,Bi³⁺ (Gd,Y,Lu,La)₂O₂S:Eu³⁺,Bi³⁺ (Gd,Y,Lu,La)VO₄:Eu³⁺,Bi³⁺ (Ca,Sr)S:Eu²⁺,Ce³⁺ ZnS:Cu⁺,Cl⁻ ZnS:Cu⁺,Al³⁺ ZnS:Ag⁺,Cl⁻ ZnS:Ag⁺,Al³⁺ SrY₂S₄:Eu²⁺ CaLa₂S₄:Ce³⁺ (Ba,Sr,Ca)MgP₂O₇:Eu²⁺, Mn²⁺ (Y,Lu)₂WO₆:Eu³⁺,Mo⁶⁺

(Ba,Sr,Ca)_(β)Si_(γ)N_(μ):Eu²⁺,Ce³⁺ (wherein 2β+4γ=3μ)

Ca₃(SiO₄)Cl₂:Eu²⁺

(Y,Lu,Gd)_(2−φ)Ca_(φ)Si₄N_(6+φ)C_(1−φ):Ce³⁺, (wherein 0≦φ≦0.5)

(Lu,Ca,Li,Mg,Y)alpha-SiAlON:Eu²⁺,Ce³⁺ 3.5MgO*0.5MgF₂*GeO₂:Mn⁴⁺

Ca_(1−c−f)Ce_(c)Eu_(f)Al_(1+c)Si_(1−c)N₃, (where 0<c≦0.2, 0≦f≦0.2) Ca_(1−h−r)Ce_(h)Eu_(r)Al_(1−h)(Mg,Zn)_(h)SiN₃, (where 0<h≦0.2, 0≦r≦0.2) Ca_(1−2s−t)Ce_(s)(Li,Na)_(s)Eu_(t)AlSiN₃, (where 0≦s≦0.2, 0≦f≦0.2, s+t>0) Ca_(1−σ−χ−100) Ce_(σ)(Li,Na)_(χ)Eu_(φ)Al_(1+σ−χ)Si_(1−σ+χ)N₃, (where 0≦σ≦0.2, 0<χ≦0.4, 0≦φ≦0.2)

For purposes of the present application, it should be understood that when a phosphor has two or more dopant ions (i.e. those ions following the colon in the above compositions), this is to mean that the phosphor has at least one (but not necessarily all) of those dopant ions within the material. That is, as understood by those skilled in the art, this type of notation means that the phosphor can include any or all of those specified ions as dopants in the formulation.

When the phosphor composition includes a blend of two or more phosphors, the ratio of each of the individual phosphors in the phosphor blend may vary depending on the characteristics of the desired light output. The relative proportions of the individual phosphors in the various embodiment phosphor blends may be adjusted such that when their emissions are blended and employed in an lighting device, there is produced visible light of predetermined x and y values on the CIE chromaticity diagram. As stated, a white light is preferably produced. This white light may, for instance, may possess an x value in the range of about 0.30 to about 0.55, and a y value in the range of about 0.30 to about 0.55. Preferably, the color point of the white light will lie on or substantially on the Planckian (also known as the blackbody) locus, e.g. within 0.020 units in the vertical (y) direction of the CIE 1931 chromaticity diagram, more preferably within 0.010 units in the vertical direction. Preferably, the CCT of the white light is less than 4500K. The general CRI (Ra) is preferably greater than 80, more preferably greater than 90. As stated, however, the identity and amounts of each phosphor in the phosphor composition can be varied according to the needs of the end user. Since the efficiency and absorption of individual phosphors may vary widely between suppliers, the exact amounts of each phosphor needed are best determined empirically, e.g. through standard design of experiment (DOE) techniques.

FIG. 17 shows a prophetic example of the power spectrum of a lighting apparatus based on a blend of the K₃[GdF₆]:Mn⁴⁺ phosphor with YAG:Ce phosphor, coupled to a semiconductor LED with peak wavelength around 470 nm, which produces a warm white light with a color point lying on the Planckian locus (0.000 in the y direction of the 1931 CIE diagram), CCT of 2700K, Ra=93.8 and LER=336 lm/W_(rad). As mentioned earlier, blends of the inventive phosphors with yellow emitting phosphors (such as YAG:Ce, TAG:Ce or BOS:Eu and their compositional modifications known in the art) represent particularly preferred embodiments of the present invention, suitable for general lighting applications.

It may be desirable to add pigments or filters to the phosphor composition. When the LED is a UV emitting LED, the phosphor layer 22 may also comprise from 0 up to about 10% by weight (based on the total weight of the phosphors) of a pigment or other UV absorbent material capable of absorbing or reflecting UV radiation having a wavelength between 200 nm and 450 nm.

Suitable pigments or filters include any of those known in the art that are capable of absorbing radiation generated between 200 nm and 450 nm. Such pigments include, for example, nickel titanate or praseodymium zirconate. The pigment may be used in an amount effective to filter 10% to 100% of the radiation generated in the 200 nm to 500 nm range.

Apart from white light blends for general illumination, these phosphors can be used either individually or in blends for LEDs for traffic signals, signage, and particularly for LCD backlighting applications. The narrow red line emission allows for a saturated color that is highly desirable for these applications.

The phosphor materials described above may be used in additional applications besides LEDs. For example, the material may be used as a phosphor in a fluorescent lamp, in a cathode ray tube, in a plasma display device or in a liquid crystal display (LCD). These uses are meant to be merely exemplary and not exhaustive.

The present development has been described with reference to various exemplary embodiments. Modifications and alteration will occur to others upon a reading and understanding of this specification. The invention is intended to include all such modifications and alterations insofar as they come within the scope of the appended claims or the equivalent thereof. 

1. A lighting apparatus for emitting light comprising: a semiconductor light source; and a phosphor material radiationally coupled to the light source, wherein said phosphor material comprises at least one phosphor selected from the group consisting of: (A) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; and (B) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=X=Sc, Y, La, a lanthanide, Bi, or a combination thereof.
 2. The lighting apparatus of claim 1, wherein the light source is a semiconductor light emitting diode (LED) emitting radiation having a wavelength in the range of from about 370 to about 500 nm.
 3. The lighting apparatus of claim 1, wherein said semiconductor light source comprises a nitride compound semiconductor represented by the formula In_(i)Ga_(j)Al_(k)N, where 0≦i; 0≦j, 0≦k, and i+j+k=1.
 4. The lighting apparatus of claim 1, wherein the light source is an organic emissive structure.
 5. The lighting apparatus of claim 1, wherein the phosphor material is coated on the surface of the light source.
 6. The lighting apparatus of claim 1, further comprising an encapsulant surrounding the light source and the phosphor material.
 7. The lighting apparatus of claim 1, wherein the phosphor material is dispersed in the encapsulant.
 8. The lighting apparatus of claim 1, further comprising a reflector cup.
 9. The lighting apparatus of claim 1, wherein said phosphor material further comprises one or more additional phosphors.
 10. The lighting apparatus of claim 9, wherein said one or more additional phosphors has an emission maximum in the range of 430 to 500 nm.
 11. The lighting apparatus of claim 9, wherein said one or more additional phosphors has an emission maximum in the range of 500 to 610 nm.
 12. The lighting apparatus of claim 11, wherein said one or more additional phosphors is one or more of a garnet activated with Ce³⁺ or an alkaline earth orthosilicate activated with Eu²⁺.
 13. The lighting apparatus of claim 9, wherein said one or more additional phosphors are selected from the group including: (Ba,Sr,Ca)₅(PO₄)₃(Cl,F,Br,OH):Eu²⁺,Mn²⁺; (Ba,Sr,Ca)BPO₅:Eu²⁺,Mn²⁺; (Sr,Ca)₁₀(PO₄)₆*νB₂O₃:Eu²⁺ (wherein 0<ν≦1), Sr₂Si₃O₈*2SrCl₂:Eu²⁺;(Ca,Sr,Ba)₃MgSi₂O₈:EU²⁺,Mn²⁺; BaAl₈O₁₃:Eu²⁺, 2SrO*0.84P₂O₅*0.16B₂O₃:Eu²⁺; (Ba,Sr,Ca)MgAl₁₀O₁₇:Eu²⁺, Mn²⁺; (Ba,Sr,Ca)Al₂O₄:Eu²⁺; (Y,Gd,Lu,Sc,La)BO₃:Ce³⁺,Tb³⁺; (Ba,Sr,Ca)₂Si_(1−ξ)O_(4−2ξ):Eu²⁺; (wherein 0≦ξ≦0.2); (Ba,Sr,Ca)₂(Mg,Zn)Si₂O₇:Eu²⁺; (Sr,Ca,Ba)(Al,Ga,In)₂S₄:Eu²⁺; (Y,Gd,Tb,La,Sm,Pr,Lu)₃(Sc,Al,Ga)_(5−α)O_(12−3/2α):Ce³⁺ (wherein 0≦α≦0.5); (Lu,Sc,Y,Tb)_(2−u−v)Ce_(v)Ca_(1+u)Li_(w)Mg_(2−w)P_(w)(Si,Ge)_(3−w)O_(12−u/2) (where −0.5≦u≦1; 0<v≦0.1; and 0≦w≦0.2); (Ca,Ba,Sr)Si₂O₂N₂:Eu²⁺,Ce³⁺; (Ca,Sr)₈(Mg,Zn)(SiO₄)₄Cl₂:Eu²⁺,Mn²⁺; Na₂Gd₂B₂O₇:Ce³⁺,Tb³⁺; (Sr,Ca,Ba,Mg,Zn)₂P₂O₇:Eu²⁺, Mn²⁺; (Gd,Y,Lu,La)₂O₃:Eu³⁺,Bi³⁺; (Gd,Y,Lu,La)₂O₂S:Eu³⁺,Bi³⁺; (Gd,Y,Lu,La)VO₄:Eu³⁺,Bi³⁺; (Ca,Sr)S:Eu²⁺,Ce³⁺; ZnS:Cu⁺,Cl⁻; ZnS:Cu⁺,Al³⁺; ZnS:Ag⁺,Cl⁻; ZnS:Ag⁺,Al³⁺; SrY₂S₄:Eu²⁺; CaLa₂S₄:Ce³⁺; (Ba,Sr,Ca)MgP₂O₇:Eu²⁺,Mn²⁺; (Y,Lu)₂WO₆:Eu³⁺,Mo⁶⁺; (Ba,Sr,Ca)_(β)Si_(γ)N_(μ):Eu²⁺, Ce³⁺ (wherein 2β+4γ=3μ); Ca₃(SiO₄)Cl₂:Eu²⁺; (Y,Lu,Gd)_(2−φ)Ca_(φ)Si₄N_(6+φ)C_(1−φ):Ce³⁺ (wherein 0≦φ≦0.5); (Lu,Ca,Li,Mg,Y)alpha-SiAlON:Eu²⁺,Ce³⁺; 3.5MgO*0.5MgF₂*GeO₂:Mn⁴⁺; Ca_(1−c−f)Ce_(c)Eu_(f)Al_(1+c)Si_(1−c)N₃, (where 0<c≦0.2, 0≦f≦0.2); Ca_(1−h−r)Ce_(h)Eu_(r)Al_(1−h)(Mg,Zn)_(h)SiN₃ (where 0<h≦0.2, 0≦r≦0.2); Ca_(1−2s−t)Ce_(s)(Li,Na)_(s)Eu_(t)AlSiN₃ (where 0≦s≦0.2, 0≦f≦0.2, s+t>0); Ca_(1−σ−χ−φ)Ce_(σ)(Li,Na)_(χ)Eu_(φ)Al_(1+σ−χ)Si_(1−σ+χ)N₃ (where 0≦σ≦0.2, 0<χ≦0.4, 0≦φ≦0.2).
 14. The lighting apparatus of claim 9, where said lighting apparatus produces white light.
 15. The lighting apparatus of claim 14, where said white light has a CCT of less than 4500K.
 16. The lighting apparatus of claim 14, where said white light has a general CRI (R_(a)) greater than
 80. 17. The lighting apparatus of claim 14, where said white light has a general CRI greater than
 90. 18. The lighting apparatus of claim 14, where said white light has a LER greater than 330 lm/W_(opt).
 19. The lighting apparatus of claim 14, where said white light has a color point lying on or substantially on the Planckian locus.
 20. The lighting apparatus of claim 19, where a color point of said white light is within 0.01 from the Planckian locus in the vertical direction on the CIE 1931 chromaticity diagram.
 21. A phosphor material comprising at least one phosphor selected from the group consisting of: (A) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; and (B) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof.
 22. A phosphor blend comprising at least one phosphor material selected from the group consisting of (A)-(B), and at least one additional phosphor: (A) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; and (B) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof.
 23. A backlight device comprising: i) a red line-emitting complex fluoride phosphor material activated with Mn⁴⁺ having a peak emission wavelength between 610 and 650 nm comprising at least one phosphor selected from the group consisting of: (A) A₂[MF₇]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and M=Nb, Ta or a combination thereof; and (B) A₃[XF₆]:Mn⁴⁺, wherein A=Li, Na, K, Rb, Cs, NH₄, or a combination thereof, and X=Sc, Y, La, a lanthanide, Bi, or a combination thereof; ii) a green emitting phosphor having a peak emission wavelength between 510 and 550 nm; and iii) either a) a blue LED chip having a peak emission wavelength between 440 and 480 nm, or b) a blue emitting phosphor having a peak emission wavelength between 440 and 480 nm and a violet to near-UV emitting LED chip having a peak emission wavelength from about 370 nm to about 440 nm.
 24. The backlight device according to claim 23, wherein said green emitting phosphor comprises an alkaline earth thiogallate, thioaluminate or a solid solution thereof activated with Eu²⁺.
 25. The backlight device according to claim 24, wherein said green emitting phosphor comprises strontium thiogallate activated with Eu²⁺. 